Oil-Resistant Asbestos Rubber Sheets
※
Manufactured from asbestos with oil-resistant rubber fillers and compressed into sheets form. Suitable as a oil-resistant jointing medium on heat installations and engine sealing.
※
Product's technical standard and use:
|
Item |
BLO01 |
BLO02 |
BLO03 |
BLO04 |
|
Tensile Strength (MPa) |
≥9 |
≥11 |
≥12.7 |
- |
|
Density (g/cm³) |
1.6~2.0 |
1.6~2.0 |
1.6~2.0 |
1.6~2.0 |
|
Compressibility (%) |
12±5 |
12±5 |
12±5 |
12±5 |
|
Rebound Rate (%) |
≥35 |
≥45 |
≥50 |
≥50 |
|
Flexibility |
not easy to beak |
|
Immersion in 20# aviation lub oil for 5h,lay up for 30min at temperature
15-30℃
|
Tensile Strength (MPa) |
≥8 |
≥9 |
≥10.8 |
≥26 |
|
Oil Absorption (%) |
≤23 |
≤23 |
≤23 |
≤9 |
|
Thickness Increase (%) |
- |
≤20 |
≤15 |
≤15 |
|
Immersion in 75# gasoline in or 3# for 5h and lay up for 5min at
temperature 15-30℃ |
Tensile Strength (MPa) |
≥6 |
≥7 |
≥7.9 |
≥14.7 |
|
Oil Absorption (%) |
≤22 |
≤22 |
≤22 |
≤15 |
|
Thickness Increase (%) |
- |
≤25 |
≤25 |
≤20 |
|
the oil
sealing property |
Temperature15-30℃,75#gasoline
or 3#jet fuel medium Aviating |
8MPa |
10MPa |
15MPa |
12MPa |
|
Scope
of Application |
Temperature (℃) |
≤150 |
≤250 |
≤300 |
≤400 |
|
Pressure (MPa) |
≤1.5 |
≤2.5 |
≤3.0 |
≤4.0 |
|
Applicable to sealing to oil. |
※ Main Specifications:
Thickness: 0.5 ~ 5.0 mm
Length: 1000 ~ 1500 mm
Width: 1000 ~ 1500 mm
|
|